Product Details:
Payment & Shipping Terms:
|
| Heat Treatment: | Annealed/Q + T | Surface Treatment: | Black/Peeled/Polished/Machined |
|---|---|---|---|
| Delivery Condition: | Forged Or Hot Rolled | Test: | SGS/Ut 100%/Element Testing |
| Shape: | Round/plate/sheet/flat Bar | Hardness: | 28 To 32 HRC |
| Flaw Detection: | CC / DD/ EE | Service: | Free Sample And 24 Hours Online |
| High Light: | plastic mould steel,p20 mold steel |
||
1.2311/ P20/ PDS-3/ 3Cr2Mo Plastic Mold Steel Round Bar (Diameter 10-350mm)
Applications
Used for various lager-sized or medium-size precision plastic mould and alloy parts.
a, Ideally suited for the production of plastic moulds;
b, Die holders, zinc die casting dies, backers, bolsters and injection moulds;
c, Shafts, rails and wear strips;
Mechanical Properties
| Properties | Metric |
| Hardness, Brinell (typical) | 300 |
| Hardness, Rockwell C (typical) | 30 |
| Tensile strength, ultimate | 965-1030 MPa |
| Tensile strength, yield | 827-862 MPa |
| Elongation at break (in 50 mm (2″)) | 20.00% |
| Compressive strength | 862 MPa |
| Charpy impact (V-Notch) | 27.1-33.9 J |
| Poisson’s ratio | 0.27-0.30 |
| Elastic modulus | 190-210 GPa |
Equivalent Grades
| GB | DIN | AISI | JIS |
| 3Cr2Mo | 1.2311 | P20 | PDS-3 |
Chemical Composition (Wt%)
| Steel Grade | C | Si | Mn | Cr | Mo | S | P |
| 1.2311 | 0.35-0.45 | 0.20-0.40 | 0.60-1.00 | 1.80-2.10 | 0.30-0.55 | ≤0.003 | ≤0.030 |
| P20 | 0.35-0.45 | 0.20-0.40 | 0.60-1.00 | 1.80-2.10 | 0.30-0.55 | ≤0.003 | ≤0.030 |
| PDS-3 | 0.35-0.45 | 0.20-0.40 | 0.60-1.00 | 1.80-2.10 | 0.30-0.55 | ≤0.003 | ≤0.030 |
Available Size (mm)
| Flat Bar Size(mm) | Round Bar Size(mm) | |||
| Thickness | Width | Length | Diameter | Length |
| 10-700 | 155-2200 | 2000-6000 | 20-200 | 2000-6000 |
Recommend Heat Treatment
| Quenching | Tempering | ||||||
| Heating temperature/℃ | Cooling way | Hardness (HRC) | Heating temperature/℃ | Cooling way | Hardness (HRC) |
||
| 850-880 | Oil Cooling | 50-52 | 580-640 | Air Cooling | 28-32 | ||
Features
a, Good hardness uniformity and polishing property,good machining properties.
b, Good integral machanical performance when under high temperature, high Corrosion resistance
c, Good heat-resistance and fatigue-resistance,very high mechanical behavior,cutting mechanical property.
d, Pre-hardened to HRC28-32, can be directly used on mould processing, shorten the construction period.
e, High putity and homogeneous structure of China's biggest ESR production base for its strict requirement in the whole process of exploitation, smelting, vacuum degassing, ESR, forging, annealing, inspection.
Physical Properties of 1.2311 P20 3Cr2Mo
Density: 0.284 lb/in3 (7861 kg/m3)
Specific Gravity: 7.86
Modulus of Elasticity: 30 x 106 psi (207 GPa)
Thermal Conductivity:
24 Btu/ft/hr/°F
41.5 W/m/°K
Machinability: 60-65% of a 1% carbon steel