Product Details:
Payment & Shipping Terms:
|
| Standard: | DIN, JIS, AISI, ASTM, GB, BS | Melting: | EAF+LF+ESR |
|---|---|---|---|
| Technics: | Hot Rolled, Forged | Flaw Detection: | CC / DD/ EE |
| Surface Treatment: | Black/Peeled/Turned | Shape: | Round Bar |
| Heat Treatment: | Annealed / Q + T | Hardness: | ＜255HBS |
| Performance: | Good Hardenability, Resistance | Cusoimized: | Yes / OEM |
| Our Service: | CIF / FOB / EXW | ||
| High Light: | international tool steel,hot work die steel |
||
Hot Rolled Hot Work Tool Steel Turned 1.2344 H13 SKD61 Turned Steel Round Bar
It's used for Die-casting mould of aluminum, extrusion mould, and thin-walled plastics mould.
1. Features
A, Good heat-resistance and fatigue-resistance.
B, Good cutting and polishing performance.
2. Application
Used for making hot squeeaing mould, forging mould and embedded lump.
A, Suitable to manufacturing aluminum, zinc, copper alloy extrusion die, die casting, hot forging die and hot shear blades, etc.
B, Extrusion mold of aluminum and magnesium, die-casting mold, especially adapt to the mold in large and complicated form.
C, Extrusion mold of copper alloy, die-casting mold
3. Heat Treatment
Quenching:
The first stage of preheating:500 ~ 550 ºC
The second stage of preheating:750 ~ 800 ºC
Cooling or high pressure gas cooling, 100 ~ 150 ºC in the tempering furnace.
Tempering:
Preheat:300 ~ 350 ºC
Tempering heating:550 ~ 680 ºC
Air cooling to room temperature, tempering three times.Quenching temperature 1000 ~ 1050 degrees, 50 to 55 HRC hardness, heat treatment deformation is small, can be nitriding surface nitriding processing, processing of products has better wear resistance.
4. SKD61 Hardness: Annealing 235 ~ 205 HB, quenching ≥50 HRC, tempering hardness 46-50HRC.
5. Delivery Detail
For abundant stock, 15-20 days.
For customized products, 30-50 days.
Package: We provide standard export packing or according to customers' request.
6. Grade
| GB(China) | AISI(America) | JIS(Japan) | DIN(Germany) |
| 4Cr5MoSiV1 | H13 | SKD61 | 1.2344 |
7. Chemical composition (%)
| C | Si | Mn | Cr | Mo | V |
| 0.38 | 1.0 | 0.5 | 5.0 | 1.4 | 1.0 |
8. Technical service:
Die nacuum heat treatment and die surface treatment (N-O, C-N, carburize and nitridation surface treatment).