Product Details:
Payment & Shipping Terms:
|
Surface Condition: | Black/Polishing | Test: | 100% UT Passed |
---|---|---|---|
Heat Treatment: | Annealed/Q+T | Process Tech.: | Hot Rolled/forged |
Material: | Alloy Structure Steel | Application: | Structure |
High Light: | engineering special steels,h13 tool steel |
Alloy Structure Steel Round Bar SAE8620 /1.6523/20CrNiMO
Grade:
America Standard: SAE8620
International Standard: 20CrNiMo2
Japan Standard: SNCM220
Europe Standard: 20NiCrMo2-2 1.6523
Chemical Composition
C | Si | Mn | Cr | Ni | Mo | S | P |
0.18-0.23 | 0.15-0.35 | 0.70-0.90 | 0.40-0.60 | 0.40-0.70 | 0.15-0.25 | ≤0.035 | ≤0.035 |
Available sizes:
Dia: Hot rolled:10-310mm; Gorged:80-800mm
Length: 3-12m as customer's request
Delivery condition:
Hot rolled or forged, Peeled(bright surface), annealed or QT(Optional)
Heat Treatment:
Soft annealing: heat to 680-720°C, cool slowly.
Hardness after annealing: Max. 241 HB
Hardening: 820 - 850 °C
Normalizing temperature: 840-880°C
Tempering: 540-680°C
Usage:
1. SAE8620 round steel high hardenability
2. No temper brittleness, weldability is very good
3. The formation of cold cracking tendency is small
4. Machinability and cold strain plasticity good
5. General quenching or carburizing quenching state use.
Features:
Hardenability similar to 20CrNi steel.
Although the content of Ni in steel is half that of 20CrNi steel, the upper part of the austenite isothermal transformation curve is shifted to the right due to the addition of a small amount of Mo. Due to the proper increase of Mn content, the hardenability of the steel is still good, and the strength Also higher than 20CrNi steel. Commonly used in the manufacture of small and medium-sized cars, tractors, engines and transmission gear in the system can also replace the 12CrNi3 steel mandrel performance requirements of high carburizing parts, cyanide pieces, such as oil drilling and metallurgical open-pit mine roller bit Tooth claw and toothed body.
20CrNiMo due to containing molybdenum in addition to a good overall performance but also resistant to a certain temperature. For manufacturing steam turbine gear rotors internal combustion engine connecting rod cross section forgings.
Heat treatment:
Quenching heating temperature (℃): 850; Coolant: oil
Tempering heating temperature (℃): 200; coolant: empty
Tensile strength σb (MPa): ≥ 980 (100)
Yield strength σs (MPa): ≥785 (80)
Elongation δ5 (%): ≥9
Section shrinkage ψ (%): ≥ 40
Impact energy Akv (J): ≥47
Impact toughness value αkv (J / cm2): ≥59 (6) Brinell hardness (HBS100 / 3000) (annealing or tempering state): ≤ 197
Delivery Status:
To heat treatment (normalizing, annealing or tempering) or non-heat treatment delivery, delivery status should be specified in the contract.