| Heat Treatment: | Annealed/Q + T | Surface Treatment: | Black/Peeled/Polished/Machined/turned |
|---|---|---|---|
| Delivery Condition: | Hot Rolled | Test: | SGS/Ut 100%/Element Testing |
| Certificate: | ISO/Mill Certificate | Shape: | Flat Bar |
| Process: | EAF+LF+VD+ESR | Payment Term: | 30% Deposit, Balance By L/C At Sigth After Shipment |
| High Light: | tool steel bar,international tool steel |
||
Hot Rolled High Carbon High Chromium Cold Work Tool Steel SKD11 / D2 / 1.2379
SKD11 cold work tool steel is a kind of high-carbon high-chromium alloy tool steel, which has high hardness after heat treatment.
It has the characteristics of strong hardenability and good dimensional stability. It is suitable for making high-precision long-life cold work die and heat Solid molding plastic mold.
Chemical composition (%)
| C | Si | Mn | Cr | Mo | V | P | S |
| 1.40-1.60 | 0.30-0.50 | 0.30-0.50 | 11.0-13.0 | 0.70-1.20 | 0.70-1.10 | ≤0.030 | ≤0.015 |
Similar grades:
| AISI | DIN | GB | JIS |
| D2 | 1.2379 | Cr12Mo1V1 | SKD11 |
Available Sizes:
| Flat Bar Size(mm) | Round bar Size(mm) | |||
| Thickness | Width | Length | Diameter | Length |
| 8-160 | 155-610 | 3000-6000 | 14-80 | 300-6000 |
Recommend heat treatment:
| Quenching | Tempering | ||||
| Heating temperature/℃ | Cooling | Hardness/HRC | Heating temperature/℃ | Cooling | Hardness/HRC |
| 980-1040 | Oil or Air | 60-65 | 180-220 | Air | 60-64 |
| 1060-1100 | 60-65 | 510-540 | Air | 60-64 | |
Main usage
SKD11 cold work tool steel is easy turning, it can be made of sharp knives, scissors, circular saws, metal stamping dies, forming rolls, cold or hot for the general cold mold dressing, drum edge, screw thread, Round drum, the system of power transformers heart die, cut steel knife, steel forming drum, special forming roller, precision gauge, complicated shape of the cold-pressure tools, metallurgy, tin mold, plastic mold and other molds.
Characteristic
1. Vacuum degassing refining Steel pure ball annealing softening
2. Cutting performance is good Wrought rolling combined with broken glass
3. Fine and uniform carbide particles
4. Don't worry about quenching and cracking strengthening elements molybdenum, vanadium special addition,
4. Excellent wear resistance.
Heat treatment
Quenching: First preheat 700 ~ 750 ℃, and then heated to 1000 ~ 1050 ℃ cooling in still air, such as the thickness of the steel over 6 inches were heated to 980 ~ 1030 ℃ hardened in the oil better.
Tempering: Heated to 150 ~ 200 ℃, stay in this temperature, and then cooled in still air.
Hardness: HRC 61 or more. Annealing: heated to 800 ~ 850 ℃, stay at this temperature for 1 to 3 hours, let it in the furnace to let it cool.
Forging: 1050 ~ 950 ℃.
About Guangzhou Changfeng Steel
Guangzhou Changfeng Steel Co., Ltd is a mould steel stockist, we have our own mould steel factory and trading company. Our main steels are carbon tool steel, plastic mold steel, hot work tool steel, cold work tool steel, Hot Rolled alloy steel for mechanical, etc.
We provide all materials with high quality and competitive price.
Contact Person: Echo
Tel: +86 18148729336
Fax: +86-020-8251-5866