Product Details:
Payment & Shipping Terms:
|
| Standard: | DIN, JIS, AISI, ASTM, GB, BS | Application: | Die Mould / Tooling / Machinery |
|---|---|---|---|
| Technics: | Hot Roll, Forged | Heat Treatment: | Annealed |
| Hardness: | 19-22 HRC | Flaw Detection: | CC / DD/ EE |
| Surface Treatment: | Optional | Shape: | Plate / Flat Bar |
| High Light: | high carbon tool steel,machining tool steel |
||
1.1210/ S50C/ SAE1050/ 50# Mold Basic Supporting Structure Carbon Tool Steel Plate
S50C is also a normal steel grade with wide application. It is close to S45C carbon steel, both in properties or in applications. Just customers in different area have different habit of S45C or S50C. Further, the cost and price for both S45C and S50C steels are slight different. You could just choose either for your own applications.
Application range of S50C Carbon Steel Materials
JIS S50C grade carbon steel is widely used in strong supporting structure of machinery manufacturing, good mechanical properties of this steel.
S50C carbon steel are generally use to make strong supporting mechanical parts, such as: spring, gear, tension bar, the roller, the axis, the load spindle and so on.
1. Features
a,High-quality medium carbon steel,uniform characteristics of the microstructure.
b,Carbon content (mass fraction,%) ≥ 0.4, good wear resistance,ductility reduction.
c,Tempering must be quenched to avoid the occurrence of temper brittleness.
d,Tempering HRC19-22
2. Equivalent Grades
| GB(China) | DIN(German) | AISI(USA) | JIS(Japan) |
| 50# | 1.1213 | SAE1050 | S50C |
3. Available Size (mm)
| Flat Bar Size(mm) | Round bar Size(mm) | |||
| Thickness | Width | Length | Diameter | Length |
| 10-700 | 155-2200 | 3000-6000 | 10-300 | 3000-6000 |
4. Chemical Composition(%)
| C | Si | Mn | P | S | Cr | Ni | Cu |
| 0.41-0.50 | 0.15-0.35 | 0.6-0.9 | ≤0.035 | ≤0.035 | ≤0.25 | ≤0.25 | ≤0.25 |
JIS S50C Steel Mechanical Properties
| Tensile Strength (MPa) |
Yield Strength (MPa) |
Elongation Ration (%) |
Reduction of area Psi(%) |
Impact merit AKV (J) |
Resilient value AKV(J/cm2) |
Hardness | Annealed |
| ≥630 | ≥375 | ≥14 | ≥40 | ≥31 | ≥39 | ≤235HB | ≤207HB |
5. Applications
1,Can be used for a variety of cold mold die pad.
2,For the manufacture of high wear resistance, dynamic load and impact of the role of small machined parts and spring pieces.
3,Standard template material.