Product Details:
Payment & Shipping Terms:
|
| Alloy Steel Grade: | 1.1210, S50C, SAE1050 | Standard: | DIN, JIS, AISI, ASTM, GB, BS |
|---|---|---|---|
| Application: | Die Mould / Tooling / Machinery | Technics: | Hot Roll, Forged |
| Heat Treatment: | Annealed | Flaw Detection: | CC / DD/ EE |
| Surface Treatment: | Optional | Shape: | Plate / Flat Bar |
| High Light: | high carbon tool steel,heat treating tool steel |
||
1.1210/ S50C/ SAE1050 Carbon Tool Steel Plate , Used for making Mold Frame
Application range of S50C Carbon Steel Materials
JIS S50C grade carbon steel is widely used in supporting structure of machinery manufacturing, good mechanical properties of this steel.
S50C carbon steel are generally use to make supporting mechanical parts, such as: spring, gear, tension bar, the roller, the axis, the load spindle and so on.
1. Features
a, High-quality medium carbon steel,uniform characteristics of the microstructure.
b, Carbon content (mass fraction,%) ≥ 0.4, good wear resistance,ductility reduction.
c, Tempering must be quenched to avoid the occurrence of temper brittleness.
d, Tempering HRC19-22
2. Equivalent Grades
| GB(China) | DIN(German) | AISI(USA) | JIS(Japan) |
| 50# | 1.1213 | SAE1050 | S50C |
3. Available Size(mm)
| Plate | Thickness (mm) | Width (mm) | Length (mm) |
| 10-350 | 2000-2200 | 4000-12000 | |
| Block | Thickness (mm) | Width (mm) | Length (mm) |
| 200-1000 | 800-1600 | 2000-6000 | |
| Round Bar | Diameter (mm) | Length (mm) | |
| 10-350 | 4000-12000 | ||
4. Chemical Composition(%)
| C | Si | Mn | P | S | Cr | Ni | Cu |
| 0.41-0.50 | 0.15-0.35 | 0.6-0.9 | ≤0.035 | ≤0.035 | ≤0.25 | ≤0.25 | ≤0.25 |
JIS S50C Steel Mechanical Properties
| Tensile Strength (MPa) |
Yield Strength (MPa) |
Elongation Ration (%) |
Reduction of area Psi(%) |
Impact merit AKV (J) |
Resilient value AKV(J/cm2) |
Hardness | Annealed |
| ≥630 | ≥375 | ≥14 | ≥40 | ≥31 | ≥39 | ≤235HB | ≤207HB |
5. Applications
1,Can be used for a variety of cold mold die pad.
2,For the manufacture of high wear resistance, dynamic load and impact of the role of small machined parts and spring pieces.
3,Standard template material.
6. Heat Treatment
JIS S50C Steel materials could be hardened by water quenching at 810-860 degree, and tempered by rapid quenching 550-650 degree