Product Details:
Payment & Shipping Terms:
|
| Standard: | DIN,ASTM,AISI,GB,JIS | Surface Treatment: | Black / Milling / Machined |
|---|---|---|---|
| Shape: | Steel Plate / Round Bar / Flat Bar | Technique: | Hot Rolled,Forged |
| HS CODE: | 722540 / 722830 | Production Route: | Ef/Eaf+Lf+Vd/ESR |
| Annealed Handness: | Hb 240-300 | Quality Control: | Ut,Metallography Detection And Other Required Test |
| Certificate: | ISO 9001:2008 ,Ut% | ||
| High Light: | cold work tool steel,tool steel plate |
||
Wear resistance tool steel & High Speed Steel Flat Bars (1.3355/SKH2/T1)
Smelting Method
Non-Vacuum Induction Furnace + LF + ESR
Feature
T1 is belong to tungsten high speed steel,T1 is a good carbide former used in high speed steels and hot forming tool steels. It is a steel gray metal that increases temperature and red hardness, prevents gain growth and improves toughness of steels.
Chemical Composition Table (%)
| Item | C | Si | Mn | S | P | W | Cr | V |
| Min | 0.73 | 0.20 | 0.10 | 17.20 | 3.80 | 1.00 | ||
| Max | 0.83 | 0.40 | 0.40 | 0.030 | 0.030 | 18.70 | 4.50 | 1.20 |
Physical Property
| Thermal Conductivity at °C | 20 | 350 | 700 |
| W/(m*K) | 32.8 | 23.5 | 25.5 |
| Density (g/cm3) | 8.70 | 8.67 | 8.60 |
Heat Treatment Instruction
| Treatment | Temperature Range | Cooling/Quenching | Notes |
| Forging | 1700-2100° F | Slow. | Cool slowly in dry sand or in other insulating media. |
| Annealing | 1600-1650° F | Cool slowly at a rate of 35° F per hour to 1000° F. | For best results, insulating media is desirable. Hold at temperature for 2 hours. |
| Stress Relieving | 1100-1300° F | Cool slowly | Stress relieve after rough machining |
| Preheating | 1500-1550° F | Preheat time in furnace is ¾ Hr. per inch of thickness. Heating up to temperature as slow as possible. | |
| Hardening | 2325-2375° F (furnace) 2275-2350° F (salt bath) | Quench in air or warm oil. To minimize quenching strains, quench in salt at 1000° F | For maximum wear resistance, harden at 2375° F. For maximum toughness and high hardness, harden at 2275° F. |
| Tempering | (See Chart) | Double tempering is recommended. The usual tempering time is 2+2 hours. Recommended temperature is 1000-1075° F for cutting tools. 1100-1200° F for shock tools |
Picture Show:
Our main products:
| STANDARD/GRADE | Flat Bar Size(mm) | Round bar Size(mm) | Technics | ||||||
| DIN | AISM | JIS | GB(China) | Thickness | Width | Length | Diameter | Length | |
| 1.121 | SAE1050 | S50C | 50# | 10-450 | 155-2200 | 2000-12000 | Forged, Hot Rolled | ||
| 1.2311 | P20 | PDS-3 | 3Cr2Mo | 10-460 | 155-2200 | 2000-10000 | 20-200 | 2000-6000 | |
| 1.2738 | P20+Ni | - | 3Cr2NiMnMo | 21-300 | 155-2200 | 2000-8000 | 20-200 | 2000-6000 | |
| 1.2379 | D2 | SKD10 | SKD10 | 10-200 | 155-810 | 2000-6000 | 14-80 | 3000-6000 | |
| 1.2080 | D3 | SKD1 | 3Cr2Mo | 10-200 | 155-810 | 2000-6000 | 20-200 | 3000-6000 | |
| 1.2083 | 420 | - | 4Cr13 | 10-500 | 155-1200 | 2000-6000 | 12-300 | 3000-6000 | |
| 1.2344 | H13 | SKD61 | 4Cr5MoSiV1 | 10-500 | 155-1600 | 2000-6000 | 16-400 | 3000-6000 | |
| 1.2510 | O1 | SKS3 | 9CrWMn | 10-200 | 155-810 | 2000-6000 | 20-200 | 3000-6000 | |
| 1.7225 | SAE4140 | SCM440 | 42CrMo | 10-280 | 155-2200 | 2000-6000 | 16-450 | 3000-6000 | |
About Us
Guangzhou Changfeng Steel Co., Ltd. is a professional special steel company, which specializing in this line in China since 2005. Our main products are Plastic Mould Steel, Hot Work Mould Steel, Cold Work Mould Steel, Alloy Structural Steel, Tool Steel, Stainless Steel, Carbon Steel and Forged Block.