Product Details:
Payment & Shipping Terms:
|
| Heat Treatment: | Annealed / Q+T | Delivery Condition: | Forged Or Hot Rolled |
|---|---|---|---|
| Test: | SGS /UT 100% / Element Testing | Shape: | Plate / Block |
| Standard: | AISI, ASTM, DIN, GB，JIS，BS | Payment Term: | 30% Deposit, Balance By T/T Or L/C At Sigth After Shipment |
| High Light: | plastic mold steel,precision ground steel plate |
||
Pre-hardened Mold Steel Plate 1.2738 / P20+Ni for Large Size Injection Mould
Pre-hardened large size injection mould, can be pollished normally, used for making high demand large plastic mould.
1. Equivalent Grades
| GB | DIN | AISI | ASSAB |
| 3Cr2NiMnMo | 1.2738 | P20+Ni | 718 |
2. Chemical Composition(%)
| Grade | C | Si | Mn | P | S | Cr | Mo | Ni |
| P20+Ni | 0.30-0.40 | 0.20-0.50 | 1.00-1.50 | ≤0.030 | ≤0.030 | 1.50-2.00 | 0.25-0.40 | 0.80-1.20 |
| 1.2738 | 0.35-0.45 | 0.20-0.40 | 1.30-1.60 | ≤0.035 | ≤0.035 | 1.80-2.10 | 0.15-0.25 | 0.90-1.20 |
|
718 |
0.32-0.45 | 0.20-0.40 | 1.10-1.50 | ≤0.030 | ≤0.030 | 1.70-2.00 | 0.30-0.55 | 0.80-1.20 |
3. Available Size (mm)
| Flat Bar Size(mm) | Round bar Size(mm) | |||
| Thickness | Width | Length | Diameter | Length |
| 21-300 | 155-2200 | 2000-6000 | 20-200 | 2000-6000 |
4. Applications
Suitable for large-scale plastic injection products,such as home appliance, computer case, telephone sets, audio PMMA products.Used for manufacturing hot-extrusion die and mandril by aluminium alloy sections,swage hammers, forging presses, forging machine, high modulus die under high temperature and shock loading
5. Features
a. Widely used plastic mould steel with excellent comprehensive mechanical properties, high hardenabiliy with good polishability.
b. To be used directly after pre-hardening, which can guarantee good usability and avoid deformation after heat treatment.
6. Recommend Heat Treatment
| Quenching | Tempering | ||||
| Heating temperature(℃) |
Cooling | Hardness/HRC | Heating temperature(℃) |
Cooling | Hardness/HRC |
| 840-870 | OIL OR AIR | ≥50 | 550-640 | AIR | 28-36 |
7. The Process Flow
a. Hot rolled or forged condition, Pre-harden &tempering , black surface
b. Hardness: 30~36HRC
c. Hot rolled technology:EAF+LF+VD
d. Forged technology: EAF+LF+VD+ESR+Forging +Q T + Machined surface
8. Delivery
For abundant stock, 15-20 days.
For customized products, 30-50 days.
Contact Person: Ms. Echo
Tel: +86 18148729336
Fax: +86-020-8251-5866