|Standard:||DIN,ASTM,AISI,GB,JIS||Heat Treatment:||Annealed / Q+T|
|Surface Treatment:||Black / Milling / Machined||Hardness:||Annealed Hbs248 Max|
|Shape:||Steel Plate / Round Bar / Flat Bar||Technique:||Hot Rolled,Forged|
international tool steel,
tool steel round bar
D3 1.2080 SKD1 Cr12 Hot Rolled Alloy Die Steel Flat Bar
D3 Tool Steel is a high-carbon, high chromium, oilhardening tool steel thatis characterized by a relatively high attainable hardness and numerous, large, chromium-rich alloy carbides in the microstructure. These carbides providegood resistance to wear from sliding contact with other metals and abrasive materials.
AISI D3 alloy steel is heat treatable and will offer a hardness in the range 58-64 HRC. After heat treatment D3 tool steel is hard, durable and dense, and is immune from sinking in use. It offers a measure of corrosion resistance when polished. In general, the applications of AISI D3 tool steel resemble those of D2 tool steel but it should be remembered that alloy tool steel D3 has better wear resistance of the two steels and is preferred for such items as shear blades. Owing to its higher wear resistance, AISI / ASTM D3 cold work steel is slightly more difficult to grind than D2 steels.
1, Steel Grade:1.2080/ D3/ SKD1/Cr12 Cold Work Mould Steel
|Size of SKD1/1.2080 Cold Work Steel|
|Plate||Thickness(mm)||Width (mm)||Length (mm)|
Used for making small impact,high quality wear cold-punching mould;
1)Used for high tolerance and long service life of all kinds of cold stamping die and cold shear blade, thread rolling plate, etc.;
2)Tabletting punches and sleeves for corrosive;
3)Suitable for complex deformation of mould;
1)High hardenability, high hardness, high wear resistance and good toughness, quenching deformation, etc;
2)Good machinablity and inoxidizability;
3)Immune from sinking in use,high resistance to heavy pressure;
Forging of D3 Cold Work Tool Steel
Pre-heat at 900-950°C then raise temperature to 1050-1100°C. Soak until uniformly heated. D3 tool steel is relatively hard at elevated temperature. Therefore, initial hammer blows must be light and the temperature must not be allowed to fall below 1020°C until the metal begins to flow. Final forging should not be done below 900°C.
Heat Treatment of D3 Cold Work Steel
D3 tool steel requires hardening and tempering to achieve maximum properties. For maximum accuracy, the parts of D3 tool steel should be stress relieved after roughing operations. Stress should be relieved at 648°C (1200°F) for one hour and cooled slowly.
Heat D3 tool steels uniformly to 850-870°C, soak thoroughly, then slow furnace cool at a rate of not more than 25°C per hour to 650°C. The parts may then be air cooled. This should result in a maximum hardness of brinell 248.
The D3 cold work steel should be cooled to room temperature and should be tempered immediately. The parts should be placed in the tempering furnace and increased slowly to the desired tempering temperature. Tempering for 1 hour per inch of thickness is required.
D3 tool steel is extremely sensitive to overheating during hardening - do not overheat.
Pre heat slowly to 800-850°C, the raise rapidly to 950-970°C and soak until completely equalised. Quench in oil.
6, Delivery Days:
For abundant stock, 7-15 days.
For customized products, 15-30 days.
D3 1.2080 SKD1 Cr12 Hot Rolled Alloy Die Steel Flat Bar picture show
7, Packing: Standard Export Packing or Customers' request
8, About Us
Guangzhou Changfeng Steel Co., Ltd. is a professional special steel company, which specializing in this line in China since 2005. Our main products are Plastic Mould Steel, Hot Work Mould Steel, Cold Work Mould Steel, Alloy Structural Steel, Tool Steel, Stainless Steel, Carbon Steel and Forged Block.
To ensure provide high quality products to customers, we have close cooperation with many Chinese first class special steel enterprises, including Baosteel Group, Dongbei Special Steel, Changcheng Special Steel, Hongsheng Heavy Industry, Xingcheng Special Steel and Daye Special Steel.
Contact Person: Echo
Tel: +86 18148729336