Product Details:
Payment & Shipping Terms:
|
| Heat Treatment: | Annealed | Test: | SGS / UT 100% / Element Testing |
|---|---|---|---|
| Delivery Condition: | Forged Or Hot Rolled Or Cold Drawn | Surface: | Black / Peeled / Turned / Grinded |
| Shape: | Round Bar / Block | Standard: | AISI, ASTM, DIN, GB |
| High Light: | hot rolled alloy steel round bar,hot rolled steel round bar |
||
GCr15 / EN31 / SUJ2 / SAE52100 / 100Cr6 Hot Rolled Steel Rod for Making Axle
1. Similar Grade: EN31, SAE52100, GCR15, SUJ2, 100Cr6
2. Main standard:
| GB | JIS | DIN | ASTM/AISI/SAE |
| GCr15 | SUJ2 | 100Cr6 | 52100 |
3. Chemical composition:
| C | Mn | Si | Cr | P | S | Ni | Cu | Mo |
| 0.95-1.05 | 0.20-0.40 | 0.15-0.35 | 1.30-1.65 | ≤ 0.027 | ≤ 0.020 | ≤ 0.30 | ≤ 0.25 | ≤ 0.10 |
4. Available Size:
| Diameter (mm) | Length (mm) |
|
16,18,20,23,25,28,30,33,35,38,40,43,45, 48,50,55,60,65,70,75,80,85,90,95,100,110, 120,130,140,150,160,170,180,190,200, 210,220,230,240,250,260,270,280 |
4000-10000 |
5. Characteristic:
Belong to a kind of high carbon chromium bearing steel which most widely used with a good performance and less alloy content. High hardenability and good comprehensive performance.Good machinability after spheroidizing annealing.High hardness,uniform organization, good wear resistance,high contact fatigue performance after quenching and tempering.And good hot working performance.
6. Main application:
For making all kinds of bearing ring and rolling element.For example; steel ball roller and ferrule of internal combustion engine, electric motorcycle, automonilrd, tractors,machine tools, rolling mill, boring machine, mining machinery, general machinery,high load and high speed roating mechanical transmission bearing.Except ball bearing and bearing ring, sometimes also ued to make tools, such as pumching die,measuring tool.
7. Heat treatment:
| Quenching | Tempering | ||
| Heating Temperature/ºC | Cooling | Hardness/HRC | Heating Temperature/ºC |
| 830-850 | Oil | 62-65 | 150-190 |