Anti Corrosion Mold Steel Plate P20 Thickness 12 - 250mm For Die Holders

China Guangzhou Changfeng Steel Co., LTD certification
China Guangzhou Changfeng Steel Co., LTD certification
Gold supplier! Arranged shipment very fast, quality is super good. They are one of our best suppliers, will do more business with them in the future!

—— Ms Nguyen Thi Hong

We bought 7 containers from them in 2017, no quality problems. The boss is very nice and professional, good business parner!

—— Mr. Wan Rusli

Good job! Shipment was arranged fast, giving lots of good suggestions before place order, saved me time and money.

—— Mrs. Natntia Jitaniyompanich

I'm Online Chat Now

Anti Corrosion Mold Steel Plate P20 Thickness 12 - 250mm For Die Holders

Anti Corrosion Mold Steel Plate P20 Thickness 12 - 250mm For Die Holders
Anti Corrosion Mold Steel Plate P20 Thickness 12 - 250mm For Die Holders Anti Corrosion Mold Steel Plate P20 Thickness 12 - 250mm For Die Holders Anti Corrosion Mold Steel Plate P20 Thickness 12 - 250mm For Die Holders Anti Corrosion Mold Steel Plate P20 Thickness 12 - 250mm For Die Holders

Large Image :  Anti Corrosion Mold Steel Plate P20 Thickness 12 - 250mm For Die Holders

Product Details:
Place of Origin: China
Brand Name: CF
Certification: ISO / Mill Test Certificate
Model Number: 1.2311, P20, PDS-3, 3Cr2Mo
Payment & Shipping Terms:
Minimum Order Quantity: Negotiable
Price: Negotiable
Packaging Details: Standard Export Packing or As per request
Delivery Time: 7-15 days
Payment Terms: T/T, L/C
Supply Ability: 1000 MT per month
Detailed Product Description
Heat Treatment: Annealed/Q + T Surface Treatment: Black/Peeled/Polished/Machined
Delivery Condition: Forged Or Hot Rolled Test: SGS/Ut 100%/Element Testing
Certificate: ISO/Mill Test Certificate Shape: Round/plate/sheet/flat Bar
Hardness: 28 To 32 HRC Flaw Detection: CC / DD/ EE
Service: Free Sample And 24 Hours Online Standard: AISI, ASTM, DIN, GB, JIS, BS
High Light:

plastic mold steel

,

precision ground steel plate

 

1.2311 P20 Prehardening Corrosion resistance Mold Steel Plate with Thickness 12-250mm

 

 

Prehardening Wear Resistance Corrosion resistance mechanical behavior 1.2311 P20 Prehardening Corrosion resistance Plastic Mold Steel plate Material is a versatile, low-alloy tool steel that is characterized by good toughness at moderate strength levels. The special purpose Prehardening  mold steel P20 steel plate is commonly used for plastic injection mold cavities and tooling and for die casting dies for zinc. P20 mold steel plate material is typically sold in the pre-hardened condition at a hardness of approximately 300 HBW. And wth good cutting mechanical property and Corrosion resistance

 

 

1.2311 P20 Prehardening Corrosion resistance Plastic Mold Steel plate Material is a versatile, low-alloy tool steel that is characterized by good toughness at moderate strength levels. The special purpose mold steel P20 steel plate is commonly used for plastic injection mold cavities and tooling and for die casting dies for zinc. P20 mold steel plate material is typically sold in the pre-hardened condition at a hardness of approximately 300 HBW.

 

P20 tool steel differs from area to area in the different countries.Europeans generally use the standard materials (1.2311 and 1.2312), while in Japan steel industry standard, PX5 is the new standard P20. And the Americas Countries, Grade steel 1.2311 P20 is the most and wide used steel grade material. In China, 3CrM2Mo is the P20 steel grade equivalent, which is in the standard GB/T 1299 tool steel specification.

 

1.2311 P20 tool steels are nitrided or carburized. These P20 mold steel materials steels are capable of being machined into complex and large dies and molds. Material P20 steel plate and round bars are mostly used in the carburized condition. The presence of chromium and nickel enhances the toughness and hardness of mold steel P20 grade material.

 

 

1.2311 P20 Mold Tool Steel Properties

 

Physical Properties

 

Density: 0.284 lb/in3 (7861 kg/m3)

Specific Gravity: 7.86

Modulus of Elasticity: 30 x 106 psi (207 GPa)

Thermal Conductivity:

24 Btu/ft/hr/°F

41.5 W/m/°K

Machinability: 60-65% of a 1% carbon steel

 

 

P20 Steel Mechanical Properties

 

Properties Metric
Hardness, Brinell (typical) 300
Hardness, Rockwell C (typical) 30
Tensile strength, ultimate 965-1030 MPa
Tensile strength, yield 827-862 MPa
Elongation at break (in 50 mm (2″)) 20.00%
Compressive strength 862 MPa
Charpy impact (V-Notch) 27.1-33.9 J
Poisson’s ratio 0.27-0.30
Elastic modulus 190-210 GPa

 

 

 

1, Features


a, Good hardness uniformity and polishing property,good machining properties.


b, Good integral machanical performance under high temperature, Corrosion resistance


c, Good heat-resistance and fatigue-resistance,high mechanical behavior,cutting mechanical property.


d, Pre-hardened to HRC28-32, can be directly used for mould processing, shorten the construction period.


e, High putity and homogeneous structure of China's biggest ESR production base for its strict requirement in the whole process of exploitation, smelting, vacuum degassing, ESR, forging, annealing, inspection.
 

 

2, Equivalent Grades

 

GB DIN AISI JIS
3Cr2Mo 1.2311 P20 PDS-3

 

 

3, Chemical Composition(Wt%)

 

Steel Grade C Si Mn Cr Mo S P
1.2311 0.35-0.45 0.20-0.40 0.60-1.00 1.80-2.10 0.30-0.55 ≤0.003 ≤0.030
P20 0.35-0.45 0.20-0.40 0.60-1.00 1.80-2.10 0.30-0.55 ≤0.003 ≤0.030
PDS-3 0.35-0.45 0.20-0.40 0.60-1.00 1.80-2.10 0.30-0.55 ≤0.003 ≤0.030

 

 

4, Available Size (mm)

 

Plate Size(mm) Flat Bar Size(mm) Round Bar Size(mm)
Thickness Width

Length

Thickness Width Length Diameter Length
10-700 1600-2200 4000-10000 10-700 155-2200 2000-6000 20-200 2000-6000

 

 

5, Applications


Used for various lager-sized or medium-size precision plastic mould and alloy parts. 


a, Ideally suited for the production of plastic moulds;


b, Die holders, zinc die casting dies, backers, bolsters and injection moulds;


c, Shafts, rails and wear strips;

 

 

 

 

Anti Corrosion Mold Steel Plate P20 Thickness 12 - 250mm For Die Holders 0

 

 

P20 mechanical behavior tool steel differs from area to area in the different countries.Europeans generally use the DIN spec-DIN EN ISO 4957 standard materials (1.2311 and 1.2312), while in Japan steel industry standard, PX5 is the new standard P20. And the Americas Countries, Grade steel P20 is the most and wide used steel grade material. In China, 3CrM2Mo is the P20 steel grade equivalent, which in the standard GB/T 1299 tool steel specification.

 

 

AISI P20 tool steels are nitrided or carburized. These P20 mold steel materials steels are capable of being machined into complex and large dies and molds by cutting mechanical property. Material P20 steel plate and round bars are mostly used in the carburized condition. The presence of chromium and nickel enhances the toughness and hardness of mold steel P20 grade mechanical behavior Wear Resistance Corrosion resistance material.

 

 

6, Packing: Standard Export Packing or As per request

 

 

 

HEAT TREATMENT

 

Forging: P20 plastic mould steel are forged at 1093°C (2000°F) down to 899°C (1650°F). Forging below 871°C (1600°F) is not recommended for these steels.

 

Annealing: Annealing takes place at 760-788°C (1400 to 1450°F) and then the steels are cooled slowly in the furnace at a temperature less than 4°C (40°F) per hour.

 

 

Stress Relieving: When dies are heavily machined, we recommend stabilising just before finish machining in order to relieve machining strains. Heat to 460-500°C. Soak well and allow to cool in the air.

 

 

Hardening: Heat the steel uniformly to 820-840°C until heated through. Quench in oil.

 

 

Tempering: Heat uniformly and soak at the tempering temperature for at least one hour per 25mm of section. Allow to cool in still air.

 

 

Carburising / Case Hardening: Tools produced from may be case hardened, which can achieve a surface hardness of 55 to 59 HRc.

 

 

Tufftriding: At 570ºC tufftriding of P20 tool steel will give a surface hardness of approximately 700HV. Allowing two hours treatment the surface hard layer will be approximately 0.1mm.

 

 

Hard Chromium Plating: To avoid hydrogen embrittlement P20 should be tempered for 4 hours at 180°C for 4 hours after hard chromium plating

 

 

Flame / Induction Hardening: Flame or induction hardening of P20 will achieve a hardness of 50 to 55HRc. Air cooling is preferable, though smaller components may require forced cooling. Temper immediately after hardening.

 

 

Cold Working:P20 plastic mould steel are capable of being readily cold worked by using conventional tooling methods with the alloy in the annealed condition.

 

 

Welding: Conventional methods are used for welding of P20 plastic mould steel.

 

 

Forming: P20 plastic mould steel can be readily formed by conventional methods in the annealed condition.

 

 

Machinability: P20 plastic mould steel have excellent machinability at about 80% that of water hardening steels.

 

 

Contact Details
Guangzhou Changfeng Steel Co., LTD

Contact Person: Echo

Tel: +8613535323261

Send your inquiry directly to us (0 / 3000)