Product Details:
Payment & Shipping Terms:
|
Standard: | DIN,ASTM,AISI,GB,JIS | Heat Treatment: | Annealed / Q+T |
---|---|---|---|
Surface Treatment: | Black / Milling / Machined | Hardness: | Annealed Hbs248 Max |
Shape: | Steel Plate / Round Bar / Flat Bar | Technique: | Hot Rolled,Forged |
HS CODE: | 722540 | ||
High Light: | alloy steel flat bar,tool steel flat bar |
AISI D3/Cr12/Assab Xw-5/DIN 1.2080 Could Work Tool Steel Flat Bar Equivalent
Hot Rolled Cold Work Tool Steel Flat Bar SKD11, 1.2379, D2, Cr12Mo1V1
Size of Tool Steel 1.2080
Diameter/Thikness(mm) | Width(mm) | Length(mm) | |
Round Bar | 16-600 | / | 3000-6000 |
Plate | 16-200 | 200-800 | 2000-5800 |
The specification can be customized. |
Chemical Compositions Of Tool Steel 1.2080
C | Si | Mn | P | S | Cr |
2.0-2.3 | Max 0.4 | Max 0.4 | Max 0.03 | Max 0.03 | 11.5-13.0 |
Similar Grade
GB | AISI | DIN | JIS | EN |
Cr12 | D3 | 1.2080 | SKD1 | X210Cr12 |
Heat Treatment
1) Forging
Preheat slowly to 750°C then increase temperature more rapidly to 1050-1100°C. Do not forge below 850°C. It is essential to cool slowly after forging, either in a furnace or in vermiculite.
2)Annealing
Soak thoroughly at 840-860°C before furnace cooling at a maximum rate of 20°C per hour down to 600°C
followed by cooling in air. To avoid scaling, box annealing in cast iron chips is preferred.
3)Stress Relieving
When tools made from 1.2344 tool steel are heavily machined or ground, the relief of internal strains is advisable before hardening to minimise the possibility of distortion. Stress relieving of this grade of steel should be done after rough machining. To stress relieve, heat the component carefully to 700°C, allow a good soaking period (two hours per 25mm of section). Cool in the furnace or in air. Tools may then be finish machined before hardening.
4)Hardening
Preheat to 780-820°C. Soak thoroughly, then increase rapidly to the hardening temperature of 1000-1030°C. When it has attained this temperature, soak for 20 to 30 minutes. Cool in air. Large sections may be quenched in oil. To reduce scaling or decarburisation, we recommend isothermal molten salt bath treatment. Preheat in salt at 780-820°C then transfer to salt bath standing at 1000-1030°C. Soak and quench into salt standing at 500-550°C. Allow to equalise, withdraw and cool in air. Alternatively, 1.2344 tool steel may be vacuum hardened or pack hardened. Tools should be tempered as soon as they become hand-warm.
5)Tempering
Heat uniformly to the required temperature allowing a soaking time of two hours per 25mm of ruling section. Withdraw from the furnace and allow to cool in air. A second tempering is strongly advised, the tool being allowed to cool to room temperature between tempers. The usual tempering range is 530-650°C depending on the hardness requirements and the operating temperature of the tool.
6)Nitriding
1.2080 tool steel can be nitrided to give a hard surface case. The steel is then very resistant to wear and erosion. Nitriding also increases resistance to corrosion. Nitriding in ammoniac gas at a temperature of 525°C will give a surface hardness approximately 1000 to 1250HV. Before nitriding the tool should be hardened and tempered at approximately 50°C above the nitriding temperature. It is important to note that with increase in penetration of the nitriding, there is a reduction in resistance to thermal shock and an increase in embrittlement.
Charateristics
After heat treatment the tool steel is hard, durable, dense, and is immune from sinking in use. It offers a measure of corrosion resistance when polished. In general, the applications of 1.2080 tool steel resemble those of 1.2379 but it should be remembered that 1.2080 has better wear resistance of the two steels and is preferred for such items as shear blades. Owing to its higher wear resistance, 1.2080 tool steel is slightly more difficult to grind than 1.2379.
Applications
As a quality tool steel 1.2080 is suitable for applications such as complex blanking and forming tools for long runs and for hard and abrasive materials. It is commonly used for other applications such as brick and tile mould liners, master hobs for cold hobbing plastic moulds, tabletting punches and sleeves for corrosive powders.
Product pictures
1.2080 SKD1 D3 Cr12 High Hardenability Alloy Steel Flat Bar for Mould and Tool
About us
Guangzhou Changfeng Steel Co., Ltd. is a professional special steel company, which specializing in this line since 2005 in China. Our main products are Plastic Mould Steel, Hot Work Mould Steel, Cold Work Mould Steel, Alloy Structural Steel, Tool Steel, Stainless Steel, Carbon Steel and Forged Block.
To ensure provide high quality products to customers, we have close cooperation with many Chinese first class special steel enterprises, including Baosteel Group, Dongbei Special Steel, Changcheng Special Steel, Hongsheng Heavy Industry, Xingcheng Special Steel and Daye Special Steel.
We have thousand tons of stock materials in our own factory and also can provide processing services to customers. We are full of export experience for many years, the product covers America, Germany, France, Italy, Turkey, Singapore, Thailand, Malaysia, Vietnam, Taiwan, and Middle-East.
FAQ
Q: Are you a manufacturer or merely a trader?
A: We are trading company act as exporting Steel Products with our own factory,
we can manufacture the products as in cutomer's requirement,wholesale and retail all kinds of domestic mould steel,the price we offered is very competitive compared with other agents.
Q: How do you guarantee the quality of your product?
A: Firstly, we can provide the certificates from the third party, such as SGS, CE,ISO if you need. Secondly, we have a complete set of inspection system and every process is checked by QC. Quality is the lifeline of enterprise survival. Third,the products we export are mainly from ShaGang group, WenFeng group, XingCheng group, DongTe group,DaYe and so on, the quality are certained.
Q: Can we visit your company and factory?
A: Yes, warmly welcome! We can book the hotel for you before you come to China and arrange our driver to our airport to pick you up when you come.
Contact Person: Ms. Echo
Tel: +86 18148729336
Fax: +86-020-8251-5866